Preparation of polyamide by condensation polymerization

Objective:

1. To study and understand the formation of polyamide (nylon) through condensation polymerization between surface technique

2. To observe the effect of external factors on molecular weight and polymer yield

 

Introduction:

Polymerization is a process of forming long and repeating organic polymer chains. Polymerization is categorized into different systems based on the mechanism and structure of polymer. Both structure and mechanism are usually required in order to clearly classify a polymer. Polymers were originally classified by Carothers (1992) into addition and condensation polymerization. However, the more recent terminology further classifies polymerization into step-growth, chain-growth and ring opening polymerization.

 

Condensation polymers are refers to the polymers that were formed from polyfunctional monomers by various condensation reactions with the elimination of some small molecules such as water. The type of end product resulting from the condensation polymerization is depends on the type of functional end group which can react. For example, the formation of polyester between a dicarboxylic acid and a diol in which two monomers are linked together and a water molecule has been produced.

clip_image002Figure 1 Condensation polymerization between a dicarboxylic acid and a diol

This process can continue adding alternatively one molecule and then the other, building the polymeric chain of hydrocarbon units that joined by ester bond. This is molecule formed from the condensation polymerization is called polyester.

 

In order for a condensation polymerization to occur continuously, the small molecules need to be removed from the system either by heating or through vacuum. However, heating would cause degradation or breaking of polymer molecules from bigger size of polymers to smaller size of polymer molecules. As a result, this will cause the formation of low molecular weight polymer. In order to overcome this problem, polymerization should be carried out at low temperature either by using the method of polymerization in solvent or polymerization between two surfaces of solution (interfacial polymerization). Many polymers can be produced at lower temperature (instead of high temperature) by using Schotten-Baumann reaction of acid chlorides.

image

 

Interfacial polymerization is refers to the condensation polymerization between two reactants is carried out at the interface of two immiscible solvents in which each containing one of the reactants. Interfacial polymerization is important because it produces the polymer with high molecular weight in a short period of time which under normal conditions of temperature and pressure. This type of polymerization could be carried out at room temperature and the types of polymers that could be formed using this technique are polyurethane, polyamide and polyurea. Thus, the formation of nylon 6,10 which is a type of polyamide that can be produced by using this method of reaction between two surfaces of immiscible solvents. This technique is extremely useful to the reactants which are not stable under the polymerization conditions by other techniques. Among the techniques of condensation polymerization, interfacial polymerization has some added advantages over the other techniques.

 

Nylon 6,10 is produced from the two monomers named sebacoyl chloride (ClOC(CH­2)8COCl) and 1,6-diaminohexane (also known as hexamethylenediamine, H2N(CH2)NH2). Sebacoyl chloride is a 10-carbon acid chloride with a –COCl group as functional group at each end. The other monomer is a 6-carbon chain with two amino groups, -NH2 at each end. Nylon 6,10 is named based on the carbon number of two monomers, in which the first number come from amine monomer while the latter one from acid chloride monomer. These two compounds are polymerized via condensation with the loss of a molecule of hydrogen chloride, as shown in the equation below:

clip_image006

 

Nylon is a term to represent synthetic polyamides. Different nylons are described by a numbering system that shows the number of carbon atoms in the monomer chains. Nylons from diamines and dicarboxylic acids are designated by two numbers in which the first representing the diamine whereas the second representing the dicarboxylic acid. In order to generate a long chain polymer and to expedite the rate of kinetic reaction, the polymerization system should be stirred vigorously to make sure that a new surface of polymer is always produced in the system. This ensures that the polymers produced would give a high percentage of yields. Both hexamethylenediamine and sebacoyl chloride are not solvents in the polymerization process between the interface of solutions. In the stirring technique, the non equilibrium system that occurs eliminates the weakness that might occur in polycondensation process such as:

1. The necessity of high temperature

2. Longer time of reaction

3. Accurate stoichiometric balance of equivalent

Physical properties of nylon 6,10:

1. Bright yellow in colour

2. Less transparent

3. Melting point of 220 °C

4. Moderate crystallinity

5. High impact strength

6. Electrical insulating ability

 

Apparatus:

100ml beaker, 10ml graduated cylinder, glass rod, thin stick

 

Materials:

60% w/v hexamethylenediamine, sebacoyl chloride, sodium laurel sulphate (soap powder)

 

Procedures:

1. 3ml sebacoyl chloride solution and 100ml of hexane (solution B) were added into a 100ml beaker.

2. 0.01g of soap powder was added into the mixture (solution A) of 3ml of hexamethylenediamine, 50ml of water and 2 drops of phenolphthalein.

3. Solution A was added carefully into solution B so as not to disturb the interface between two solutions.

4. A layer of polymer was formed between solution A and solution B. The strand of polymer (nylon) was wrapped around the glass rod and nylon strand was winded onto the rod with a steady pace.

clip_image008

5. The polymer formed was rinsed with water.

6. Let it dry in the oven.

7. The weight of polymer was measured.

8. The steps above were repeated with 5ml of solution B and 3ml of solution A. The solutions were stirred.

9. The polymers formed were characterized and compared.

 

Results and calculations:

Table 1 Observation on polymers that made with different methods

Observations on polymers formed with different methods

Wrapping on glass rod

White, long and weak elasticity nylon was formed.

Stirring

A clump of nylon was formed.

Table 2 Weight of polymer obtained by wrapping on glass rod

Weight of empty watch glass

20.4850 g

Weight of (empty watch glass + polymer, Nylon 6,10)

20.9122 g

Weight of polymer (nylon 6,10)

0.4272 g

Table 3 Weight of polymer obtained by stirring

Weight of filter paper

0.4836 g

Weight of (filter paper + polymer, Nylon 6,10)

0.9099 g

Weight of polymer (nylon 6,10)

0.4263 g

 

Calculate percentage yield

Unstirred interfacial polymerization

Types of monomer

hexamethylenediamine

Sebacoyl chloride

Density (g cm-3)

0.84

1.121

Volume used (cm3)

3.00

3.00

Molecular weight (g mol-1)

116.00

239.00

 

Mass of hexamethylenediamine = 0.84 g/cm3 x 3cm3 x 60% = 1.512g

Theoretical number of mole of hexamethylenediamine = 1.512g / 116 g mol-1

= 0.013 mol

Mass of sebacoyl chloride = 1.121 g/cm3 x 3cm3 = 3.363g

Theoretical number of mole of sebacoyl chloride = 3.363g / 239 g mol-1

= 0.014 mol

Thus, limiting agent is hexamethylenediamine.

Molecular weight of repeating unit = 282 g mol-1

Weight of nylon 6,10 obtained experimentally = 0.4272g

Actual number of mole of repeating unit = 0.4272g / 282 g mol-1 = 0.0015 mol

Percentage yield = 0.0015 mol / 0.013 mol x 100%

= 11.54%

 

Stirred interfacial polymerization

Types of monomer

hexamethylenediamine

Sebacoyl chloride

Density (g cm-3)

0.84

1.121

Volume used (cm3)

3.00

5.00

Molecular weight (g mol-1)

116.00

239.00

Mass of hexamethylenediamine = 0.84 g/cm3 x 3cm3 x 60% = 1.512g

Theoretical number of mole of hexamethylenediamine = 1.512g / 116 g mol-1

= 0.013 mol

Mass of sebacoyl chloride = 1.121 g/cm3 x 5cm3 = 5.605g

Theoretical number of mole of sebacoyl chloride = 5.605g / 239 g mol-1

= 0.023 mol

Thus, limiting agent is hexamethylenediamine.

Molecular weight of repeating unit = 282 g mol-1

Weight of nylon 6,10 obtained experimentally = 0.4263g

Actual number of mole of repeating unit = 0.4272g / 282 g mol-1 = 0.0015 mol

Percentage yield = 0.0015 mol / 0.013 mol x 100%

= 11.54%

 

Table 3 Comparisons between two polymers that produced by different methods

Wrapping on the glass rod

Method to produce polymers

Stirring by using glass rod

0.4272g

Mass

0.4263g

11.54%

Percentage yield

11.54%

More elastic

Elasticity

Less elastic

Stronger

Stiffness (Malleability)

Weaker

Stronger

Ability to stick to surface

Weaker

 

Discussion:

In this experiment, the interfacial polymerization technique plays a very important role. This method is primarily used in the case of condensation polymers, in which two reactants have different solubility characteristics. Hexamethylenediamine and sebacoyl chloride were used in this experiment in order to demonstrate the condensation polymerization in the interface between two solutions.

 

Interfacial polymerization is different from the usual condensation polymerization. This is because the monomers (undergo this polymerization) tend to diffuse to the interface and will only react with the polymer chain end formed initially. The diacid chloride and diamine monomer molecules will react with the growing polymer chain end before they penetrate through the polymer film to create the growth of new polymer chains. Therefore, interfacial polymerization creates a high tendency to generate high molecular weight polymer in the polymerization process. In addition, stoichiometry automatically exists at the interface because both monomers diffuse from aqueous phase and organic phase respectively. The stoichiometry at the interface is perfectly controlled by mass transfer controlled rate of diffusion and consumption of each monomer species.

 

Sebacoyl chloride was placed in 100ml of hexane (solution B) while hexamethylenediamine was added with 50ml of water (solution A). The introduction of aqueous layer and organic layer was used to create an interface between two solutions since aqueous layer and organic layer will not mix together. Interfacial polymerization occurs instantly forming a thin film of solid nylon 6,10 at the interface. The thin film at the interface stops further reaction by preventing the monomers to meet each other. During the preparation of solution B, any apparatus used should be rinsed with hexane and thus they do not contain water. If water present, chloride ion, Cl- of sebacoyl chloride tend to react with the hydroxide, OH- in water to form sebacic acid as well as two hydrochloric acid molecules.

clip_image010

The reaction between sebacoyl chloride and water is very reactive since chloride ion is a group leaving group.

 

A small amount (0.01g) of sodium laurel sulphate (soap powder) was introduced into the solution B in order to lower the surface tension of solution A and hence hexamethylenediamine will easily solubilize in it. As a result, the condensation polymerization is encouraged to occur in the interface. Since hexamethylenediamine exists its base property in the presence of water, so two drops of phenolphthalein was added as an indicator to show the position of interface between the solutions and to determine the point where hexamethylenediamine has been used up. In alkaline solution, the colour of phenolphthalein is pink while it will be faded if the alkalinity of solution decreases.

 

The interface between solution A and solution B should not be disturbed during transferring the solution A into solution B. This is to make sure both reactants do not form a polymer clump in unstirred interfacial polymerization. The system contains two layers in which solution A with hexamethylenediamine is upper layer whereas solution B with sebacoyl chloride is the lower layer because sebacoyl chloride is denser than hexamethylenediamine. During the transferring process, condensation polymerization between hexamethylenediamine and sebacoyl chloride took place at the interface is shown as the equation below:

clip_image012

At the interface between the solutions, a bigger molecule was formed from the reaction between both monomers and two small molecules hydrochloric acid, HCl were generated. The bigger size molecule formed at the interface could be dimer, trimer, tetramer, oligomer and polymer.

 

In unstirred interfacial polymerization, the colour of phenolphthalein indicator was faded as more nylon was wrapped on the glass rod and finally it was decolourized. This is because the decrease in concentration of hexamethylenediamine in which the diamine was polymerized in the system. In addition, the condensation polymerization produced hydrochloric acid as by-product and it neutralized the acid present in the system. The increase of hydrochloric acid concentration caused the phenolphthalein indicator to be decolourized. In stirred interfacial polymerization, the pink colour of phenolphthalein decolourized immediately once both solutions were stirred. This method produced a polymer clump in the solution. As the time pass, the polymer clump was predicted to become smaller because the hydrochloric acid will hydrolyze the amide bond in the polymer molecule.

 

By comparing both polymers that produced from two methods, the nylon 6,10 in unstirred polymerization results a more elastic and stiffer polymer than the nylon 6,10 in stirred polymerization. Besides, its ability to stick on the wall of beaker and surface is stronger when compared to nylon obtained from the latter method. The molecular weight of nylon obtained in unstirred polymerization is predicted to have higher molecular weight since its mechanical strength is greater than the other one. The weight of nylon 6,10 obtained in the unstirred interfacial polymerization was 0.4272 g while the weight of nylon 6,10 obtained via stirred interfacial polymerization was 0.4263g. Both methods gave the same percentage yield of 11.54%.

 

Reference:

1. Odian, G. (2004). Principles of Polymerization (4th Ed.). USA: John Wiley & Sons, Inc.

2. Wagh, S.J., & Jadhav K.T. (n.d.) A review on interfacial polycondensation:

types, applications andeffect of various parameters.

3. Ji, J., Childs, R.F., & Mehtra, M. (2001) Mathematical model for encapsulation by interfacial polymerization. 192 (2001), P 55-70.

15 comments:

  1. Wow. First time i read this reaction. Interesting. Thanks for sharing.

    - Mr Acetate

    ReplyDelete
  2. I have done a similar experiment in school, but the results obtained are completely opposite. The mass of nylon 6,10 in unstirred polymerization is less than that in stirred polymerization. :(

    ReplyDelete
    Replies
    1. Probably you have to re-do it and justify. Take note on the amount of reagents added.

      Delete
  3. may i know, how do you get 60% in the calculation of mass above?

    ReplyDelete
  4. Unfortunately my english didn't help me to understand the relation between the interfacial polymerization and the condensation polymerizaion.
    is the interfacial polymerization a technique used in the condensation polymerization , or they are the same process with different terms?

    ReplyDelete
  5. This comment has been removed by the author.

    ReplyDelete
  6. May I know why the mass of nylon 6,10 in stirred polymerization is less than that in unstirred polymerization?

    ReplyDelete
  7. Very good article
    i have detailed article below discussing about Pilot Plant and how they are designed Pilot Plant design .
    I have also written about scaling up the Pilot plant Pilot plant scale up
    Also Reactor design has been explained in detail here Reactor Design along with Adiabatic Reactor design Adiabatic Reactor Design

    ReplyDelete
  8. very nice blog. from www.chemeasylearn.blogspot.com

    ReplyDelete
  9. Do you mind if I quote a couple of your articles as long as I provide credit and sources back to your website? My website is in the exact same niche as yours and my users would really benefit from a lot of the information you provide here. Please let me know if this ok with you. Thanks a lot! Lift Up Bros

    ReplyDelete
  10. Myself Manish Diwakar from Agra. I am currently doing S E O service Agra, India. I am working on offline pages. Manīṣh Diwākar (Seo Agra)

    ReplyDelete
  11. Myself Manish Diwakar from Agra. I am currently doing S E O service Agra, India. I am working on offline pages. Manīṣh Diwākar (Seo Agra)
    #bookmarkingsubmission #directorysubmission #articlessubmission #pressreleasesubmisison
    Thanks and best regards
    Manish Diwakar
    www.manishdiwakaragra.blogspot.com
    ☎+91-7456830678

    ReplyDelete